Products

 poliester

Polyester Foams have lower flexibility properties. Their Push-Release curves are far from each other. However, they have higher physical resistances. They are more durable against abrasion, friction, tear and more resistant against chemicals (such as detergents, fry cleaning solvents) as well. Therefore, they are used in the fields where rather technical requirements are prominent such as automotive industry, sound insulation, painting works etc. One of the important fields of use is textile industry (wadding, brassiere). They are preferred in cloth laminations because they are very suitable for flame lamination process. In addition to sunlight endurance it is higher than other foams and another important property is their capability of being shaped by being hot pressed. This property is very important in the preparation of automotive cases. Polyester Foam can also be manufactured in “special types”. The most popular special types are car washing Foam and Hydrophilic Foam.

Car washing Foam:

It is solid and has big pores. They were used for scratching and cleaning the insects which stick the windows of the automobiles in the long distances and named after that. Today, they are used in wall paint applications and other cleaning works.

Hydrophilic Foam:

These foams draw water into their body and keep it there. They are used in impregnation works, cosmetics and cleaning works.

Type of Foams Density
kg/m3
ISO 845
Firmness (N)
ISO 2439
(ILD%40)
Firmness
ASKER F
Tensile Strength (kPa)
İSO 1789
Elongation at Break (%)
ISO 1789
Tear Resistance 
(N/cm) ASTM.D 3547
Flame Rate (cm/dak)
MVSS 302
Number of Cell
(ad/Inc)

D22 POLYESTER

22±2

180±%15

43 (+\-%15) 120

185

5

≤18

36±5

D23 POLYESTER

23±2

188±%15

45 (+\-%15) 120

185

5

≤18

38±5

D23 POLYESTER SERT

23±2

210±%15

50 (+\-%15) 135

145

5

≤18

38±5

D24 POLYESTER

24±2

195±%15

47 (+\-%15) 120

180

4,5

≤15

40±5

D24 CAM SÜNGERİ

24±2

220±%15

53 (+\-%15) 70

80

3

≤20

24±5

D26 POLYESTER

26±2

150±%15

- 115

120

4

≤15

40±5

D28 POLYESTER

28±2

160±%15

39 (+\-%15) 150

185

5

-

40±5

D30 POLYESTER

30±3

210±%15

51 (+\-%15) 120

175

4

≤12

43±5

D30 POLYESTER LOWFOG

30±3

210±%15

51 (+\-%15) 120

175

4

≤12

38±5

D33 POLYESTER

33±3

160±%15

- 115

125

4

-

43±5

D35 POLYESTER

35±3

180±%15

- 120

130

4,5

-

43±5

D40 POLYESTER

40±3

210±%15

- 125

135

4

-

44±5

D45 POLYESTER

45±3

250±%15

60 (+\-%15) 110

135

3,5

≤11

48±5

D50 POLYESTER

50±3

250±%15

60 (+\-%15) 120

150

4

≤11

48±5